 Click to enlarge image
|
- Only One Time Recycled
- Nearly Same Quality Against prime resin
- 30~40% Cheaper than prime resin
Typical Properties
|
Property
|
Unit
|
Test
Condition
|
Test
Method
|
High Impact
|
|
HI-100
|
HI-100H
|
HI-121
|
HI-121H
|
HI-151
|
HI-153
|
|
Mechanical
|
|
Tensile Strength
|
kg/cm2
|
50mm/min
|
ASTM
D638
|
380
|
400
|
480
|
530
|
510
|
520
|
|
Elongation
|
%
|
50mm/min
|
D638
|
30
|
25
|
25
|
20
|
20
|
20
|
|
Flexural Strength
|
kg/cm2
|
15mm/min
|
D790
|
600
|
700
|
750
|
800
|
850
|
800
|
|
Flexural modulus
|
kg/cm2
|
15mm/min
|
D790
|
18,500
|
21,000
|
23,000
|
26,000
|
25,000
|
26,000
|
|
Izod impac Strength
|
kg.cm/cm
|
Notched1/4"
Notched1/8"
|
D256
|
40
50
|
45
53
|
30
35
|
22
24
|
20
24
|
17
22
|
|
Rockwell hardness
|
|
R-Scale
|
D785
|
90
|
105
|
103
|
108
|
106
|
112
|
|
Thermal
|
|
Heat Deflection Temp
|
°C
|
Unannealed
18.5kg/cm2
1/2"
|
D648
|
90
|
90
|
91
|
92
|
92
|
92
|
|
Vicat Softening Temp
|
°C
|
1,000g
|
D1525
|
97
|
97
|
98
|
99
|
96
|
96
|
|
Flammability
|
|
1/8"
1/16"
|
UL94
|
HB
HB
|
HB
HB
|
HB
HB
|
HB
HB
|
HB
HB
|
HB
HB
|
|
mm.min
|
1/8"
|
IEC707
|
FH3-33
|
|
FH3-34
|
FH3-34
|
FH3-32
|
FH3-30
|
|
Physical
|
|
Specific Gravity
|
|
|
ASTM
D792
|
1.05
|
1.05
|
1.05
|
1.05
|
1.05
|
1.05
|
|
Molding Shrinkage
|
%
|
|
D955
|
0.4
~0.7
|
0.4
~0.7
|
0.4
~0.7
|
0.4
~0.7
|
0.4
~0.7
|
0.4
~0.7
|
|
Melt Flow Index
|
g/10min
|
220°C/10kg
|
D1238
|
10
|
12
|
18
|
20
|
20
|
38
|
|
Electrical
|
|
HWI
|
PLC Code
|
|
UL 746A
|
3
|
|
3
|
3
|
3
|
3
|
|
HAI
|
PLC Code
|
|
UL 746A
|
4
|
|
0
|
2
|
0
|
0
|
|
HVTR
|
PLC Code
|
|
UL 746A
|
2
|
|
2
|
2
|
1
|
0
|
|
Arc Resistance
|
PLC Code
|
|
ASTM
D495
|
6
|
|
6
|
6
|
5
|
6
|
|
CTI
|
PLC Code
|
|
UL746A
|
0
|
|
0
|
0
|
0
|
1
|
|
Characteristics
|
|
|
|
Super
high
impact
|
Super
high
impact
(Helmet)
|
High
impact
|
High
impact
high
whiteness
|
Middle
impact
|
Weather
resistance
high gloss
|
|
|
|
|
| |
|
|
|
Related Keywords: